P20 Steel Supplier In Gurugram. Buy at the best price.

P20 Steel Supplier In Gurugram offer By Jaiganeshsteel.com.

Premium grade P20 Steel Supplier In Gurugram.

WHAT IS P20 STEEL?

P20 steel is a versatile and low-alloy tool steel.

It is generally characterized by its good toughness at moderate strength levels.

The P20 steel is used for plastic injection mould cavities.

and also for tooling as well as for die casting dies for zinc.

HOW HARD IS P20 STEEL?

This steel is almost equivalent to injection mould steels.

and also with good reason.

From the base steel, It is available with 50-plus HRC hardness.

It can also be case hardened to the high 50’s HRC and also readily nitrided to 60HRC.

When hardness and corrosion resistance is needed.

Up to half a millimetre of case depths is possible.

Contact details of P20 Steel Supplier In Gurugram.

Jai Ganesh Steel Company

  • Address: B 40, PhaseI, Mayapuri Industrial Area, New Delhi -110064

  • Phone:-:011-45872912, +91-9015270017,  +91-8802688030

  • Email ID:-: [email protected]

P20 Steel Supplier In Gurugram. Buy alloy steel at the best price
largest and oldest P20 Steel Supplier In Gurugram.

Jai Ganesh Steel was offering to the Buy alloy steel at the best price.

DO YOU KNOW WHAT IS MOULD STEEL?

With a combination of Carbon, Chromium, Manganese and Molybdenum,

Not well as being pre-hardened.

This steel is the most popular steel for mould making.

It is also used for compression moulds and plastic injection,

Similarly also for zinc die casting dies.

Moulds made with this steel can be directly placed into the service.

P20 Steel Supplier In Gurugram from since 1978.

WHAT IS HEAT TREATMENT OF P20 STEEL?

The various methods of heat treatment are as follows:-

  • Stress Relieving.
  • Hardening.
  • Austenitizing (High Heat).
  • Quenching.
  • Tempering.
  • Annealing.

WHAT IS STRESS RELIEVING OF P20 STEEL?

As the P20 steel for mould is sold in the pre-hardened condition.

hardening through heat treatment is not necessary.

But after machining and intermittently during service,

steel must be thermally stress relieved, by heating it to 900ºF (482ºC).

holding and equalizing for an hour per inch (25.4mm) of thickness.

after that cooling in air to ambient temperature.

NOTE:- In rare circumstances where the AISI steel is re-hardened.

Prior to hardening, first, the steel must be annealed.

WHAT IS HARDENING OF P20 STEEL?

Hardening of steel means to make the steel harder.

for that, it is heated to very high temperature.

The amount of carbon present in the metal.

decides the final hardness of the steel.

Only steel that has high carbon content can be hardened and tempered.

For Hardening:-
Critical Temperature: Ac1: 1405ºF (763ºC).
Preheating of Steel: Heat the steel at a rate not exceeding 400ºF (222ºC) to 1150-1250ºF (621-677ºC)per hour and equalize.

WHAT IS AUSTENITIZING OF P20 STEEL?

Austenitizing means to heat the steel at high heat temperature.

Heat the steel rapidly from the preheat to 1550ºF (843°C) temperature.

For the first inch of thickness, soak for 30 minutes.

and then 15 minutes for each additional inch.

WHAT IS QUENCHING OF P20 STEEL?

The process of decreasing the fluorescence intensity of a given substance is known as Quenching.

For Quenching methods are:-

  • Pressurized gas.
  • Interrupted oil.

WHAT IS TEMPERING TEMPERATURE OF P20 STEEL?

It is tempered at 482-593°C (900 to 1100°F).

WHAT IS ANNEALING OF P20 STEEL?

Annealing of this steel takes place at 760-788°C (1400 to 1450°F).

after that, the steels are slowly cooled in the furnace at a temperature less than 4°C (40°F) per hour.

customize size P20 Steel Supplier In Gurugram, Noida and Delhi.

WHO IS THE LEADING P20 SUPPLIER IN GURUGRAM?

Jaiganeshsteel is the leading supplier of p20 steel in Gurugram.

We believe in the quality steel supply.

and customer satisfaction.

tested grade P20 Steel Supplier In Gurugram.

we are the leading custom size manufacturer and supplier in Gurugram.

For steel, Contact us:- jaiganeshsteel